Daylight damage-saving time
Analytical results and method for organic solar cell after 100 h light irradiation Credit: Kanazawa University

Researchers at Kanazawa University have performed a detailed investigation of the molecular mechanisms by which organic solar cells suffer damage as they are exposed to sunlight. This research has important implications for developing next-generation solar panels that combine high efficiency, low cost, and long device lifetimes.

Solar power represents an important element of future renewable energy solutions. Historically, have tended to be inefficient or else too expensive for most homeowners to consider installing. A new class of solar cells that utilizes layers of carbon-based polymers offers efficiency of up to 10%—which is considered the minimum for practical use—at an affordable price point. The primary remaining obstacle to wide adoption of these new photovoltaics is the short lifetime of these devices because cumulative damage from the sun tends to erode their performance. Owing to the multilayer nature of the devices, it is often difficult to identify molecular mechanisms by which this degradation of efficacy occurs over time.

Now, based on the results of current-voltage curves, impedance spectroscopy, and UV-VIS spectrophotometry, a research team at Kanazawa University has determined an important factor that can cause reduced performance. Similar to the way your carbon-based skin cells can get a nasty sunburn from the sun's ultraviolet light after a day at the beach, the researchers found that the fragile organic molecules in the semiconducting layer can be damaged from exposure.

"We found that damage from UV light increased the electrical resistance of the organic semiconductor layer," first author Makoto Karakawa says. This led to reduced current flow and thus an overall decrease in efficiency. Using a method known as matrix assisted laser desorption/ionization time-of-flight, the researchers determined the likely degradation products from solar damage. When some sulfur atoms in the materials get replaced by oxygen atoms from the atmosphere, the molecules no longer function as intended.

"While new organic semiconductor materials have allowed us to drastically increase overall efficiency, we found that they tend to be more fragile to UV damage," senior author Kohshin Takahashi explains. Based on this understanding, it may be possible to design more robust devices that still maintain their high energy conversion rate, which is an important step to making solar an even larger portion of renewable energy generation.

More information: Makoto Karakawa et al, Factors contributing to degradation of organic photovoltaic cells, Organic Electronics (2019). DOI: 10.1016/j.orgel.2019.105448

Citation: Daylight damage-saving time (2019, December 2) retrieved 28 March 2024 from https://phys.org/news/2019-12-daylight-damage-saving.html
This document is subject to copyright. Apart from any fair dealing for the purpose of private study or research, no part may be reproduced without the written permission. The content is provided for information purposes only.

Explore further

Ternary acceptor and donor materials increase photon harvesting in organic solar cells

6 shares

Feedback to editors